Download or read book Characterization and Growth Analysis of Two Types of Thin Films Formed on Copper Surfaces written by Belinda L. Hurley and published by . This book was released on 2004 with total page pages. Available in PDF, EPUB and Kindle. Book excerpt: Abstract: Surface enhanced Raman scattering was used to observe interactions of dilute CrVI solutions with silver and copper surfaces in situ. Using silver as a model surface, CrIII was observed at the near monolayer level, and the spectra were compared to those from CrIII oxyhydroxide species and CrIII/CrVI mixed oxide. Similar experiments were conducted with copper surfaces and 785 nm excitation. Upon exposure of a copper surface to CrVI solution, the characteristic copper oxide Raman bands disappeared, and a CrIII band increased in intensity over a period of %7E20 hours. The intensity of the CrIII band on copper became self limiting after the formation of several CrIII monolayers, as supported by chronoamperometry experiments. This CrIII spectrum was stable after CrVI was removed from the solution provided the potential remained negative of -200 mV vs. Ag/AgCl. The results support the conclusion that CrVI is reductively adsorbed to copper at the near neutral pH and open circuit potentials expected for Cu/Al alloys in field applications. The CrIII film is stable and strongly inhibits oxygen reduction at the treated copper surface. Copper surfaces and polished Aluminum Alloy 2024 T3 substrates were derivatized at open circuit potential with arenediazonium salts in both aprotic and aqueous media. Raman spectroscopy confirmed the presence of a derivatized film on the substrates before and after exposure to boiling water and sonication in acetone. Preliminary experiments to test these films for corrosion inhibition proved unsuccessful. Aluminum and copper substrates were prepared and used for x-ray photoelectron spectroscopy (XPS) analysis of the derivatization results. In the copper experiments, one surface was native oxide copper, predominantly in the form of Cu2O, and one surface was predominantly Cu0. Results of the XPS analysis indicate the presence of a Cu-O-C linkage and possibly a Cu-C covalent bond between the aryl ring and the copper substrate. XPS results also indicate the formation of multilayers on both types of copper surfaces with different percentages of azo coupling within the multilayers on the two surfaces. These easily prepared, covalently bonded organic films could be used for applications currently fulfilled with self-absorbed monolayers and Langmuir Blodgett films.